INCREASE WEAR RESISTANCE HARD ALLOYS T15K6 BORIDE COATINGS
The results of studies on the application of complex boron coating powder method on hard alloys. Defined phase and chemical composition, thickness and microhardness of the coating on alloys.
It was established that after diffusion saturation of hard alloy in boron mixture for 4 hours formed coating with boride phases TiB, WB, CoB and WC, TiC, whose thickness is 50-60 microns. At complex saturation with boron and copper for 4 hours diffusion saturation formed coating with boride phases TiB, WB, CoB and WC, TiC and separate inclusions of copper with a thickness of the diffusion layer up to 70-80 microns.
Boriding and complex saturation with boron and copper allows in 2 – 2.5 times increase the microhardness of the surface layers of hard alloys, that in turn leads to increased wear resistance.