Peculiarities of the interaction of a highly carbonized ferrochrome with iron during sintering of 65% Fe-35% FH800 composite
The influence of temperature of sintering on structure formation, phase composition, microhardness of components of powder composite 65 % wt. Fe – 35 % wt. FH800 were investigated. It has been established that the increase in the temperature of sintering from 1050 ºС to 1250 ºС leads to some increase in volumetric shrinkage, density and decrease in porosity of samples of material which was made from coarse-grained source powders of industrial production components. It was found that the sintering of green compacts in the range of 1000-1300 ºС causes significant changes in the chemical and phase composition of the carbide component of the composite, which are described by a series of phase transformations: M7C3 → M3C (1000-1150 ºС) → M7C3 (1200 ºС) → M3C (1250-1300 ºС)