Effect of work hardening and recrystallization annealing on structure and properties of low-carbon steel wire

  • 1 Institute for problems in material science NAS of Ukraine

Abstract

In this work it was studied the influence of low-carbon steel wire annealing at different temperatures from 500 to 750 °C that was obtained by cold drawing on its structure and properties. It was sown that bigger work-hardening during the drawing process leads to the decreasing of collective recrystallization starting temperature, which could resulting in obtaining less plastic properties than are appear after lower annealing temperatures with additional loss of strength. The found effects give valuable information for cases when it is desirable to obtain the minimal strength or the maximum plasticity of the wire.

Keywords

References

  1. Alaneme K.K. Recrystallization mechanisms and microstructure development in emerging metallic materials: A review / K. K. Alaneme, E. A. Okotete // Journal of science: Advanced materials and devices. – 2019. – Vol. 4. № 1. – P. 19– 33.
  2. Соколов С.Ф. Исследование и моделирование эволюции микроструктуры и сопротивления деформации сталей при горячей обработке давлением // Диссертация на соискании степени к.т.н. – Санкт-Петербург: Политехнический университет: 2013.
  3. Lefevre-Schlick F., Brechet Y., Zurob H.S., Purdy G., Embury D. On the activation of recrystallization nucleation sites in Cu and Fe. /. F. Lefevre-Schlick, Y. Brechet, H.S. Zurob, G. Purdy, D. Embury // Mater. Sci. Eng. A. – 2009. – Vol. 502. – P.70–78.
  4. Humphreys F.J. Recrystallization and related annealing phenomena. / F. J. Humphreys, M. Hatherly // Oxford, U.K.: Pergamon Press Ltd. – 1997. – 333 p.
  5. Золоторевский Н.Ю. Моделирование структурных превращений в металлических материалах / Н. Ю. Золоторевский // СПбГПУ. – 2007. – 164 с.
  6. Martin J. W. Stability of microstructure in metallic systems. / J. W. Martin, R. D. Doherty, B. Cantor // Cambridge : Cambridge University Press. – 1997. – 442 p.
  7. Hansen N. New discoveries in deformed metals. / N. Hansen // Mater. Trans. – 2001. – Vol. 32A. № 12. – P. 2917 – 2919.
  8. Effect of cold rolling and annealing on mechanical properties of HSLA steel / [I. Schindler, M. Janošec, E. Místecký, M. Rùièka et. all.] // Arch. Mater. Sci. Eng. – 2009. - Vol. 36. № 1. – P. 41 – 47.
  9. Humphreys F.J. Nucleation in recrystallization / F.J. Humphreys // Mater. Sci. Forum. – 2004. – P. 107 – 116.
  10. Haasen P. Physical metallurgy / P. Haasen // Cambridge : Cambridge University Press. – 1997. – 2740 p.
  11. Горелик С.С. Рекристаллизация металлов и сплавов. / С. С. Горелик, С. В. Добаткин, Л. М. Капуткина // М.: Изд-во МИСИС – 2005. – 432 с.
  12. Tavakoli M. Static recrystallization kinetics of ferrite in cold-deformed medium carbon steel / M. Tavakoli, H. Mirzadeh, M. Zamani // Mater. Res. Express. – 2020. – Vol. 6. № 12. – P. 1265 – 1273.
  13. Каверинский В.В. Моделирование кинетики распада переохлаждѐнного аустенита в легированных сталях / В. В. Каверинский, А. И. Троцан, З. П. Сухенко // Металлофизика и новейшие технологии. – 2017. - № 8. – С. 1051 – 1068.
  14. Соколов Д.Ф. Эмпирические формулы для расчѐта температур и концентраций углерода, отвечающих параравновесию основных фаз в сталях / Д. Ф. Соколов, А. А. Васильев, Н.Г. Колбасников, С. Ф. Соколов // Вопросы материаловедения. – 2012. – Т. 69. № 1. – С. 5 – 13.
  15. Каверинський В.В. Математичне моделювання і комп’ютерний аналіз процесів структуроутворення легованих сталей в ході фазових перетворень // Київ: КІМ. – 2019. – 212 с.

Article full text

Download PDF