The possibility of control of efficiency of different factors of high voltage electric discharge (HVED) impact on Ti – Al – С powders system for aimed synthesis of dispersion-hardening components is shown. Nanolaminate-composite Ti₃AlC₂ – TiC with hardness of HV5 = 7 GPa, obtained by consolidation of blend of 85 % Ti + 15 % Al initial composition after HVED with the use of multi-point electrode system has needle structure of Ti₃AlC₂ (a = 0.3068 nm, c = 1.844 nm) with size up to 10 μm, and TiC dispersion-hardening phase (a = c = 4.4331 nm) with particle size no more than 1 μm is situated between grains of Ti₃AlC₂. Dynamic strength of specimens depending on electrode system used during HVED treatment of blend variated in range from 160 to 620 MPa, Young modulus – from 13 to 22 GPa at deformation rate from 600 to 900 s–1. Material has high levels of heat resistance, relative change of mass is no more, than 0.001.

Peculiarities of titanium carbide obtainment by high voltage electric discharge synthesis (HVED) are considered in present paper. Mathematical and physical modelling of processes that occur during HVED impact on “Ti powder – hydrocarbon liquid” disperse system is performed. HVED creates thermodynamic conditions for pyrolysis of hydrocarbon liquid with formation of solid-phase carbon and gaseous hydrogen and for synthesis of titanium carbide during reaction of carbidization between titanium and carbon particles. Regularities of connection between HVED parameters and changes of dispersity and intensity of titanium carbide formation.

The effect of filler concentration of the powder mixture (Ti-TiC-C), synthesized by high-voltage electric discharge (HVED), on the thermal and mechanical properties of epoxy composites, was studied. Basing on the value analysis of destructive stresses in bending (σ), Young’s modulus (E), resilience (W) and heat resistant by Martens (T), a range of powder mixture (Ti-TiC-C) concentration, which allows to increase thermophysical and mechanical properties of epoxy composites for manufacturing equipment in conditions of alternating loads was set.