The possibility of synthesizing the Ti3AlC2 and Ti2AlC MAX phases by SPS (spark-plasma sintering) consolidation of the charge obtained as a result of mechanoactivation and a charge obtained by HVED (high-voltage electric discharge) of processing titanium and aluminum powders in kerosene has been experimentally studied. The influence of the charge activation method on phase formation and physical properties of consolidated materials is shown.

A complex approach to obtainment of titanium carbide hard metals, which consists of utilization of high density energy flows of high voltage electric discharges (HVED) for dispersion and activation of particles of powders mixture of 80 % Ti + 20 % Fe composition and synthesis of carbide phase and subsequent consolidation of obtained powders mixture by high density electric current with spark plasma sintering (SPS) method. Connection between specific cyclic energy of treatment of “kerosene – Ti + Fe powders mixture” disperse system and changes of dispersity, shape and phase composition of powders and physical and mechanical properties (hydrostatic density, hardness, thermal conductivity, wear resistance, dynamic strength) of materials consolidated from them is found. Tungstenless titanium carbide hard metals, which have high specific values of strength and wear resistance, hardness of which is higher than 82 HRA, and thermal conductivity of such materials is insignificantly lower than thermal conductivity of VK6 alloy, were obtained

Peculiarities of titanium carbide obtainment by high voltage electric discharge synthesis (HVED) are considered in present paper. Mathematical and physical modelling of processes that occur during HVED impact on “Ti powder – hydrocarbon liquid” disperse system is performed. HVED creates thermodynamic conditions for pyrolysis of hydrocarbon liquid with formation of solid-phase carbon and gaseous hydrogen and for synthesis of titanium carbide during reaction of carbidization between titanium and carbon particles. Regularities of connection between HVED parameters and changes of dispersity and intensity of titanium carbide formation.