In view of the practical applications of the piezoelectric ceramics produced from barium titanate (BaTiO3) and barium stannate (BaSnO3), (the BT-BS system), the dielectric behavior of such materials was studied. The starting components (powder of both BaTiO3 and BaSnO3) were synthesizedand structurally characterized in аdvance. Bulk samples of BT-BS (formed as tablets with addition of PVA plasticizer) were prepared using the sol-gel method by varying the BT-BS composition percentage. The samples were characterized by complex electrical impedance spectroscopy and dielectric spectroscopy in the frequency range from 0.1 Hz to 1 MHz. As compared to BaTiO3, an increase with at least 50 % was measured for the value of the room-temperature dielectric constant (e′ – the real part of the dielectric permittivity) of the BT-BS samples containing 15 wt% BaSnO3. In contrast, the 50 wt% content of BaSnO3 led to a decrease of ′ value of BT-BS by a factor of 3.5, due to relatively low e′ value of BaSnO3. Analyses of the frequency spectra of complex electrical impedance and complex dielectric permittivity revealed the dielectric relaxational behavior of the BaTiO3+BaSnO3 system. The results obtained for ′ of BT-BS dielectrics as a function of the temperature were correlated with the data from structural studies. In particular, a specific enhancement of e′ was observed in temperature range around 120C for the BT-BS samples containing 15 wt% BaSnO3. Corresponding conclusions were done. The effects observed show that the synthesized BaTiO3-BaSnO3 ceramics are promising materials for piezoelectric and dielectric applications, e.g., in energy storage devices.

The aim of the present work is to study the characteristics and conditions of obtaining thin films in the BaTiO3–BaSnO3 system, deposited by the sol-gel method on monolithic multilayer samples. In laboratory conditions, the structure, phase composition, micromorphology, electrophysical parameters of the prepared experimental samples were studied. The existing possibilities for optimizing the applied technological regime for the synthesis and surface deposition of thin-layer coatings with set characteristics have been analyzed.

A system based on BaTiO3 – BaSnO3 (BT-BS) has been developed in search of highly efficient lead-free piezoelectric ceramics. The powder samples were mixed and homogenized in a ratio of 50%: 50% and 15%: 85%. From the compositions thus obtained, tablets with the presence of a PVA plasticizer were formed, which were further annealed in a furnace with a corundum backfill. The temperature regime is in two steps. Drying time up to 800oC with a delay of 1h 30min. and additional heating to 1150°C with one hour delay. The results were characterized by XRD analysis, the relative dielectric constant of the two samples was determined.